bainite
美 ['be?na?t] 
英 ['be?na?t]
英漢解釋
例句
Bainite also occurs during thermal treatments at cooling rates too fast for pearlite to form, yet not rapid enough to produce martensite.
貝氏體期間也發生在熱處理冷卻速度太快珍珠巖形式，還沒有足夠的迅速產生馬氏體。
Weld metal is composed mainly of acicular ferrite , granular bainite and a small amount of martensite.
焊縫金屬主要有針狀鐵素體+粒狀貝氏體+少量馬氏體組成。
To sum up, the upper bainite characterize pearlite decomposition, while the lower bainite has the impression of martensite transformation.
從整體上看，上貝氏體具有某些珠光體分解的特征；而下貝氏體則具有馬氏體相變的特征。
The chemical composition, organization and properties of the newly developed quasi- Bainite cast steel are described.
介紹新研制的準貝氏體鑄鋼的化學成分、組織及性能特點。
Effects of different cooling medium on microstructure and mechanical properties of bainite wear resistant steel plate were investigated.
研究了不同冷卻介質對貝氏體耐磨鋼板組織和力學性能的影響。
NEW AUSTENITE-BAINITE STEEL WITH NODULAR EUTECTICS AND ITS IMPACT ABRASIVE WEAR RESISTANCE?
新型團球狀共晶體奧氏體貝氏體鋼及其抗沖擊磨料磨損特性？
The microstructure, properties and wear resistance of carbide-free bainite wear-resistant casting steel were investigated.
研究了無碳化物貝氏體耐磨鑄鋼材料的組織、力學性能和耐磨性能。
The microstructure of the weld bonds is a combination of martensite, lower bainite and retained austenite.
焊接熔合區組織為馬氏體+下貝氏體+殘余奧氏體；
Essentially, hardness lag of the alloyed Bainite ductile cast iron resulted from solute drag-like effect.
貝氏體球墨鑄鐵有性能滯后現象，其實質是溶質類拖曳作用。
MPa grade RPC steel is the recently developed new generation steel, which has ultra-fine bainite and better mechanical properties.
RPC鋼是一種具有超細的貝氏體組織和較好力學性能的新一代鋼鐵材料。
Solute atoms may be segregated in pre-bainite period and solute- depleted region may be nucleation site.
貝氏體預相變期發生溶質原子偏聚，貧溶質區即形核位置。
The formation of upper bainite ferrite was investigated with TEM, The much smaller lamellate subunits was observed.
觀察到貝氏體條由更小的薄片狀亞單元組成。
With the isothermal holding time prolonged, the thick rod-like upper bainite associated and gradually developed into featherlike bainite.
隨著等溫時間的進一步延長，粗棒狀上貝氏體平行排列組合具有近似羽毛狀；
Test results show that non-metallic inclusion and bainite structure in the steel are main factors affecting the elongation.
試驗結果表明：鋼中非金屬夾雜物和貝氏體組織是影響伸長率的主要因素。
Influence of different heat treatment process on microstructure and properties of bainite steel has been investigated.
研究熱處理對新型貝氏體鋼的組織與力學性能的影響。
The reason of temper brittleness belong with bainite ferrite and retain austenite decompose carbide.
500℃回火出現回火脆性，其原因與組織中的貝氏體、鐵素體及殘余奧氏體分解形成碳化物有關。
By controlling knock-out time, bainite structure was obtained in the as - cast low - carbon ductile iron cast with EPC process.
采用消失模鑄造工藝，經準鑄態貝氏體工藝處理后，得到了貝氏體組織。
When the crack meets the hard phase bainite, it spreads along the edge of the bainite.
裂紋在擴展過程中遇到硬質相貝氏體時沿其邊緣行走。
The intermedium temperature microstructure of medium carbon alloy steel is upper and lower bainite.
中碳合金鋼的中溫轉變組織只有上、下貝氏體。
The strengthening of X100 pipeline steel mainly depend on bainite transformation and precipitation strengthening.
X100管線鋼的強化機制主要為組織細化和貝氏體相變強化。
The effect of austenitizing temperature on structure and properties of vanadium bainite ductile cast iron is studied in present research.
研究奧氏體化溫度對含釩貝氏體球墨鑄鐵組織和性能的影響。
Ce can increase the transformation temperature of bainite and enlarge intervals of bainite.
鈰會使貝氏體轉變點升高，同時加大了貝氏體轉變間隔；
Spring steel strip for coupling and drive parts , watch springs , bainite- hardened parts .
接頭及驅動器零件彈片鋼帶、手表彈片、貝氏體淬火零件鋼帶。
The centrifugal compound casting process of needle-like bainite ductile iron roller was establish in this paper.
本文制定了針狀貝氏體球鐵離心復合軋輥的生產工藝。
The ferrite is obtained first through annealing, then biphase structure of ferrite and bainite is obtained through isothermal quenching.
其經預先退火得到全部鐵素體組織，然后等溫淬火得到鐵素體和貝氏體雙相組織的基體。
Ferrite(F) zone, pearlite(P) zone, bainite (B) zone and martensite(M) zone were found on both CCT diagrams.
兩種CCT曲線上均有鐵素體區（F）、珠光體區（P）、貝氏體區（B）和馬氏體區（M）。
The morphology and distribution of vanadium in bainite ductile cast iron were studied.
研究了釩在貝氏體球墨鑄鐵中的存在形態及其分布。
The nature of bainite changes as the transformation temperature is lowered.
性質的改變貝氏體轉變溫度降低。
Brief Discussion on Nucleation and Growth in Bainite Formation--Reply to Prof. Kang Mo-kuang et al.
簡論貝氏體相變的形核與長大--復康沫狂教授等。
The result show that the microstructure formed after thermal cycle was mainly lath bainite and granular bainite in CGHAZ .
結果表明：在不同的焊接熱循環條件下，焊接粗晶區組織主要是板條貝氏體和粒狀貝氏體。
New Martensite- Bainite nodular cast iron will be continued development.
新型馬貝球鐵在未來將會得到繼續發展。
The micro-structure of fracture surface of HAZ is of granular bainite, with characteristics of coarse crystal zone.
熱影響區斷口表層剖面組織為粒狀貝氏體，顯示出粗晶區的特征。
The morphology of bainite and toughness was investigated in CGHAZ of the high Nb X80 pipeline steel after simulated weld thermal cycle.
采用熱模擬技術研究高鈮X80管線鋼的在不同的焊接熱循環條件下的貝氏體組織的轉變及沖擊韌性的變化。
The paper studied the resistance flashing welding process for bainite alloy rail with PD3 rail.
研究了貝氏體合金鋼軌與PD3鋼軌兩種異種材料閃光對接焊工藝。
Additionally, the transformation zone of bainite is sealed up at the right side.
貝氏體轉變區的右側端部封口等。
A kind of the grinding ball from bainite white iron as -cast was achieved by all oing and metal molding.
采用合金化、金屬型快冷手段獲得鑄態貝氏體白口鐵磨球。
The reason is that the content of bainite with low toughness is decreased in the weld with the increasing of welding speed.
這是因為焊接速度增加能使得焊縫中低韌性上貝氏體含量減少，從而提高了焊縫的強度。
The effect of granular bainite, ferritepearlite on the strength, ductility and toughness of lowcarbon steel was investigated.
在化學成分相同的條件下，分別研究了粒狀貝氏體、鐵素體珠光體對低碳合金鋼強度、塑性、沖擊韌性的影響。
The U75V(PD3) rail was repaired by welding in the cold condition with JD-960(bainite welding rode) as overlaying welding.
本文研究在冷焊條件下，采用JD-960焊條（貝氏體焊條）直接堆焊修復U75V（PD3）鋼軌。
in the other hand, the lower bainite transformation is inseparable to martensite transformation.
而下貝氏體轉變與馬氏體相變有密切的聯系。