The annealing temperature has significant effect on microhardness of AZ31, however, the time of annealing has no effect.
退火處理溫度對AZ31鎂合金的硬度值有顯著影響，但退火處理時間的影響卻不明顯。
The high frequency induction hardening can't raise the surface microhardness of the cold precision forging spur gear.
高頻感應淬火不能達到硬化冷精鍛直齒圓柱齒輪齒面的目的。
After ultrasonic impact, the surface microhardness and the section microhardness are obviously increased.
沖擊后接頭的表面和斷面顯微硬度均得到了提高。
The microhardness distribution of the welded joint is along the welding line. The microhardness is higher in nugget zone, and lowest in HAZ.
焊接接頭的硬度分布沿焊縫中心基本對稱，焊核區(qū)硬度較高，熱影響區(qū)硬度最低。
The microhardness is higher and grain size is smaller in weld bead zone, compared with the heat-affected zone and base metal.
相對母材和熱影響區(qū)，焊縫的晶粒明顯細小，顯微硬度比熱影響區(qū)和母材稍高。
The microhardness of the cladding layer was measured by microhardness tester, and its microstructure was observed by SEM.
利用維氏硬度計測試了其顯微硬度，用掃描電鏡分析了激光熔覆層的微觀形貌。
The deposition rate, microhardness, corrosion rate of low temperature iron plating layer at different temperatures are investigated.
研究了在不同溫度下獲得的低溫鍍鐵層的沉積速率、顯微硬度、腐蝕速率等性能。
The result showed that the microhardness, finish and time of strengthening layers related to parameter of strengthening technology.
試驗結(jié)果表明，表面強化層硬度、表面光潔度和強化時間與選擇工藝參數(shù)有關；
The hardening layer was analyzed by metalloscope, microhardness, electronic probe and transmission electron microscopy.
用金相顯微鏡、顯微硬度計、電子探針和透射電鏡對硬化層進行分析。
The deforming principle of fine blanking is analyzed from streamlines microstructure and microhardness of the testing part.
通過試件流線、金相組織以及顯微硬度等方面對精沖變形的機理進行了分析和研究。
The nickel plating deposited on the conversion coating has high microhardness, which can provide good protection for the magnesium alloy.
轉(zhuǎn)化膜上沉積的鍍鎳層具有較高的顯微硬度，可以對鎂合金基體起到良好的防護作用。
The microhardness can be improved at lower temperature, but deposition rate and corrosion resistance will be reduced.
溫度降低時可提高鍍層硬度，但沉積速率和耐蝕性均下降；
The depth and microhardness distribution of alumetizing layer obtained on different technical conditions were measured.
測定了不同工藝條件下獲得的浸滲層深度和浸滲層顯微硬度的分布。
The experimental results showed that the wear resistance, and microhardness were improved obviously by process.
結(jié)果表明，該項技術(shù)大大地改善了這種合金的表面耐磨性和顯微硬度。更詳細。
The morphology, properties and microstructure of the coatings were studied by SEM, XRD, and microhardness tester.
用掃描電鏡、X射線衍射儀和顯微硬度計分析了電火花表面強化層形貌、性能和組織結(jié)構(gòu)。
The feasibility of this method is confirmed by comparison with microhardness method.
在與硬度法的對比試驗中，進一步驗證了電阻法的可行性。
POWDER METALLURGY. SINTERED METAL MATERIALS EXCLUDING HARDMETALS. MEASUREMENT OF VICKERS MICROHARDNESS.
粉末冶金.硬金屬除外的燒結(jié)金屬材料.維氏顯微硬度的測定
Microhardness, depth profile and wear mechanisms were investigated by means of MVK H12, TALYSURF6, XPS and microscopy.
采用顯微硬度、輪廓深度、XPS、顯微鏡觀察等研究磨損機理。
microhardness of coatings increased with increased spraying distance linearly.
而噴涂距離對涂層顯微硬度的影響呈弱線性遞增的關系。
The microhardness treated by plasma heat treatment is notably improved, and the wear resistance and operating life increase obviously.
處理后的表面硬度有顯著提高，并明顯提高了發(fā)動機缸體的耐磨性和使用壽命。
Microstructure and surface morphology of the oxynitriding layers were studied by SEM, XRD, microhardness tester and digital camera.
利用SEM、XRD、顯微硬度計和數(shù)碼相機等研究氧氮共滲層的微觀組織、結(jié)構(gòu)及表面形貌。
The microhardness of the processed zone is lower than the cast metal, but further uniform microhardness is observed in the processed zone.
攪拌摩擦加工后，加工區(qū)的顯微硬度較鑄態(tài)區(qū)降低，但分布比較均勻；
The measured values of microhardness were calculated using mathematical statistic method.
使用數(shù)理統(tǒng)計的方法對顯微硬度測試值進行了處理。
The copper deposit also represented higher microhardness and better corrosion resistance.
電鑄銅的顯微硬度和抗腐蝕性能均明顯提高。
The microhardness distribution on cross section at both sides of the interface changed smoothly.
斷面上微觀硬度分布在界面兩側(cè)變化平緩。
The microstructure, microhardness and wear resistance of compound region were observed and measured.
對復合區(qū)進行顯微組織觀察及分析、顯微硬度測量、耐磨性能測試。
The microhardness and surface roughness increase with the shot peening intensity increase.
硬度和粗糙度都隨噴丸強度的增加而增大。
Vickers hardness testing of resistance spot, projection and seam welds (low load and microhardness).
電阻點焊、凸焊和滾焊的維氏硬度試驗（低荷載和超微硬度）
The microhardness and wear resistance of the implanted layer were determined.
對注入層的顯微硬度和耐磨性進行了測試。
The microhardness of twin spot laser welded joint is higher than that of single spot laser welded joint, but lower than that of base metal.
雙光點激光焊接頭各區(qū)域硬度低于母材，但高于單光點激光焊接頭；
Further increase of aging temperature and time could lead to the growth of the secondary phase and thus decrease of microhardness.
繼續(xù)升高時效溫度或延長時效時間會引起第二相長大而導致顯微硬度的升降。
The hardness of the coating was tested using vickers microhardness tester.
涂層硬度采用顯微硬度儀進行測試；
On the basis of the microhardness variation, the HAZ is divided into five subregions .
根據(jù)顯微硬度的變化，將焊接HAZ分為五個區(qū)段。
And in the same condition, the microhardness and wear-resistance of plastic artificial tooth descended slightly.
在相同浸泡條件下，塑料義齒的顯微硬度變化輕微，且耐磨性下降不明顯。
The depth and microhardness of strengthening layer is increased, With increasing working elastic current, but the microha. . .
且隨工作電流的增加，強化層的深度增加，表面硬度下降，次表層硬度增大且硬化層的耐磨性大幅度提高。
The microhardness of weld metal zone, HAZ and base metal decrease in totality after heat treatment.
焊縫區(qū)、熱影響區(qū)與母材的顯微硬度整體呈下降趨勢；
Both FZ and HAZ have higher microhardness than the base metal has, and microhardness in fusion centre zone is the lowest.
熔合區(qū)和熱影響區(qū)的顯微硬度顯著高于母材，焊縫中心區(qū)在整個焊縫部分硬度最低。
Metallic and other inorganic coatings - Vickers and Knoop microhardness tests.
冶金和其他非有機鍍層.維氏硬度計和努氏顯微硬度試驗機
But the microhardness of the weld bead after heat treatment reduces by 60 HV, compared with origin welded joint.
與原始接頭顯微硬度值相比，經(jīng)歷高溫熱處理后接頭的顯微硬度降低約60HV左右。
For the nickel deposit, microhardness increased 90% and tensile strength increased 130%.
電鑄鎳的顯微硬度和抗拉強度分別提高90%和130%。